本司出售的塑胶均可随货提供物性数据、SGS报告 、RoHS(环保)报告、MSDS(出厂证明)报告以及UL黄卡。FDA, LFGB,生物相溶性报告，均可开增值税
POM500AF有哪些性能
500AF
规格级别： 耐磨, 增强 注塑
产品用途： 齿轮、衬套、凸轮和耐磨擦的应用。
备注说明： 加工特性：一般等级,添加20% TEFLON3纤维，表面润滑。 产品特性：与500相似的物理性能，但有超低的磨擦系数与高度耐磨耗率。
500AF 物性表
| 吸水量 | ASTM D-570 | ||
| (浸渍平衡点) | 0.72 | % | |
| (24小时浸渍) | 0.20 | % | |
| (50%相对湿度) | 0.18 | % |
| 模收缩 (3.2mm) | 1.9-2.2 | % | |
| 比重 | 1.54 | ASTM D-792 |
| 破裂点拉伸变形量 (100℃) | 160 | % | ASTM D-638 |
| 拉伸强度 (70℃) | 32 | MPa | ASTM D-638 |
| 破裂点拉伸变形量 (-55℃) | 10 | % | ASTM D-638 |
| 挠曲疲劳忍耐限度 (50%RH,23℃,10周期) | 24 | MPa | ASTM D-671 |
| 拉伸强度 (-55℃) | 74 | MPa | ASTM D-638 |
| 挠曲系数 (100℃) | 830 | MPa | ASTM D-790 |
| 压缩应力 (23℃,10%变形) | 90 | MPa | ASTM D-695 |
| 弹性系数 (23℃) | 2890 | MPa | ASTM D-638 |
| 拉伸强度 | ASTM D-638 | ||
| (23℃) | 48 | MPa | |
| (122℃) | 19 | MPa | |
| 挠曲系数 | ASTM D-790 | ||
| (-55℃) | 3730 | MPa | |
| (122℃) | 585 | MPa | |
| 破裂点拉伸变形量 (70℃) | 40 | % | ASTM D-638 |
| 挠曲变形强度 (23℃) | 72 | MPa | ASTM D-790 |
| 破裂点拉伸变形量 (122℃) | 190 | % | ASTM D-638 |
| 负载变形量 (140kg/cm,50℃) | 0.6 | % | ASTM D-621 |
| IZOD冲击试验 (缺口-40℃) | 32 | j/m | ASTM D-256 |
| 拉伸强度 (100℃) | 23 | MPa | ASTM D-638 |
| 洛氏硬度 | 78 | M scale | ASTM D-785 |
| IZOD冲击试验 (23℃) | 37 | j/m | ASTM D-256 |
| 挠曲系数 | ASTM D-790 | ||
| (23℃) | 2410 | MPa | |
| (70℃) | 1380 | MPa | |
| 压缩应力 (23℃,1%变形) | 31 | MPa | ASTM D-695 |
| 洛氏硬度 | 118 | R scale | ASTM D-785 |
| 破裂点拉伸变形量 (23℃) | 15 | % | ASTM D-638 |
| 抗剪强度 (23℃) | 55 | MPa | ASTM D-732 |
| 抗拉伸冲击强度 (长试片23℃) | 66 | kj/m | ASTM D-1822 |
| 介电强度 (瞬间Short time(2.3mm)) | 15.8 | kv/mm | ASTM D-149 |
| 介电因数 (50%RH,23℃,10Hz) | 0.009 | ASTM D-150 | |
| 容积电阻率 (23℃,0.2%含水量) | 3×10 | Ω.cm | ASTM D-257 |
| 抗电弧 (3.1mm) | 183 | sec | ASTM D-495 |
| 介电常数 (50%RH,23℃,10-10Hz) | 3.1 | Ω.cm | ASTM D-150 |
| 线性热膨胀系数 (-40-29℃) | 10.4 | 10-5m/m℃ | ASTM D-696 |
| 热畸变温度 (1.8MPa) | 118 | ℃ | ASTM D-648 |
| 熔点 | 175 | ℃ | ASTM D-2133 |
| 热畸变温度 (0.5MPa) | 168 | ℃ | ASTM D-648 |
| 自燃性 | HB | UL 94 | |
| 线性热膨胀系数 (60-104℃) | 12.2 | 10-5m/m℃ | ASTM D-696 |