500T
POM | 聚甲醛#赛钢美国杜邦规格级别： 注塑
产品用途： 需要较好韧性的一般机械零件。
备注说明： 加工特性：一般表面润滑等级。 产品特性：韧性与DELRIN 100相近，低磨耗，但刚性与强硬度些微降低。
大量供应POM塑料原料
500T 物性表
| 吸水量 | ASTM D-570 | ||
| (24小时浸渍) | 0.31 | % | |
| (50%相对湿度) | 0.27 | % | |
| 比重 | 1.39 | ASTM D-792 | |
| 吸水量 (浸渍平衡点) | 0.75 | % | ASTM D-570 |
| 模收缩 | 1.7-1.9 | % |
| 挠曲变形强度 (23℃) | 70 | MPa | ASTM D-790 |
| 洛氏硬度 | 117 | R scale | ASTM D-785 |
| 线性热膨胀系数 (60-104℃) | 12.4 | 10-5m/m℃ | ASTM D-696 |
| 拉伸强度 (122℃) | >16 | MPa | ASTM D-638 |
| 挠曲系数 | ASTM D-790 | ||
| (100℃) | 690 | MPa | |
| (23℃) | 2420 | MPa | |
| (70℃) | 1260 | MPa | |
| 抗剪强度 (23℃) | 49 | MPa | ASTM D-732 |
| IZOD冲击试验 (缺口-40℃) | 106 | j/m | ASTM D-256 |
| 破裂点拉伸变形量 | ASTM D-638 | ||
| (122℃) | >505 | % | |
| (-55℃) | 22 | % | |
| 拉伸强度 (70℃) | >38 | MPa | ASTM D-638 |
| 负载变形量 (140kg/cm,50℃) | 0.9 | % | ASTM D-621 |
| 拉伸强度 (-55℃) | 99 | MPa | ASTM D-638 |
| 挠曲系数 (-55℃) | 3670 | MPa | ASTM D-790 |
| 拉伸强度 (100℃) | >23 | MPa | ASTM D-638 |
| 压缩应力 (23℃,1%变形) | 16 | MPa | ASTM D-695 |
| 抗拉伸冲击强度 (长试片23℃) | 835 | kj/m | ASTM D-1822 |
| 破裂点拉伸变形量 (23℃) | 91 | % | ASTM D-638 |
| 挠曲疲劳忍耐限度 (50%RH,23℃,10周期) | 25 | MPa | ASTM D-671 |
| 弹性系数 (23℃) | 2330 | MPa | ASTM D-638 |
| IZOD冲击试验 (23℃) | 143 | j/m | ASTM D-256 |
| 破裂点拉伸变形量 (100℃) | >585 | % | ASTM D-638 |
| 挠曲系数 (122℃) | 420 | MPa | ASTM D-790 |
| 洛氏硬度 | 79 | M scale | ASTM D-785 |
| 破裂点拉伸变形量 (70℃) | >545 | % | ASTM D-638 |
| 压缩应力 (23℃,10%变形) | 82 | MPa | ASTM D-695 |
| 拉伸强度 (23℃) | 58 | MPa | ASTM D-638 |
| 容积电阻率 (23℃,0.2%含水量) | 2.3×10 | Ω.cm | ASTM D-257 |
| 介电因数 (50%RH,23℃,10Hz) | 0.016 | ASTM D-150 | |
| 介电常数 (50%RH,23℃,10-10Hz) | 3.6 | ohm-cm | ASTM D-150 |
| 抗电弧 (3.1mm) | 120 | sec | ASTM D-495 |
| 介电强度 (瞬间Short time(2.3mm)) | 15.1(2.3) | kv/mm | ASTM D-149 |
| 熔点 (ASTM D-2133) | 175 | ℃ | |
| 自燃性 | HB | UL-94 | |
| 热畸变温度 (1.8MPa) | 85 | ℃ | ASTM D-648 |
| 线性热膨胀系数 | ASTM D-696 | ||
| (104-160℃) | 15.7 | 10-5m/m℃ | |
| (29-60℃) | 12.0 | 10-5m/m℃ | |
| 热畸变温度 (0.5MPa) | 174 | ℃ | ASTM D-648 |
| 线性热膨胀系数 (-40-29℃) | 10.2 | 10-5m/m℃ | ASTM D-696 |