基础创新美国 CX7110 PC/ABS 抗撞击性 高流动性 合计塑料
CX7110 PC ABS 物性表
| 比重 | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| 密度 | 1.19 g/cc | 0.0430 lb/in3 | ISO 1183 |
| 水分吸收 | 0.100 % | 0.100 % | 23°C / 50% RH; ISO 62 |
| 饱和吸水率 | 0.20 % | 0.20 % | ISO 62 |
| 线性成型收缩率,Flow | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm | 0.0040 - 0.0060 in/in @Thickness 0.126 in | SABIC Method |
| 熔体流动速率 | 22 g/10 min @Load 2.16 kg, Temperature 260 °C | 22 g/10 min @Load 4.76 lb, Temperature 500 °F | ASTM D1238 |
| 化合物熔体指数 | 21 g/10 min @Load 2.16 kg, Temperature 260 °C | 21 g/10 min @Load 4.76 lb, Temperature 500 °F | MVR [cm^3/10 min]; ISO 1133 |
| 抗张强度(断裂) | 51.0 MPa | 7400 psi | 50 mm/min; ISO 527 |
| 54.0 MPa | 7830 psi | Type I, 50 mm/min; ASTM D638 | |
| 抗张强度(屈服) | 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 |
| 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D638 | |
| 伸长率 (断裂) | 90 % | 90 % | Type I, 50 mm/min; ASTM D638 |
| 90 % | 90 % | 50 mm/min; ISO 527 | |
| 屈服伸长率 | 4.0 % | 4.0 % | Type I, 50 mm/min; ASTM D638 |
| 4.0 % | 4.0 % | 50 mm/min; ISO 527 | |
| 拉伸模量 | 2.70 GPa | 392 ksi | 1 mm/min; ISO 527 |
| 2.90 GPa | 421 ksi | 50 mm/min; ASTM D638 | |
| 弯曲强度 | 100 MPa | 14500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 100 MPa | 14500 psi | 2 mm/min; ISO 178 | |
| 弯曲模量 | 2.50 GPa | 363 ksi | 2 mm/min; ISO 178 |
| 2.70 GPa | 392 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 悬壁梁缺口冲击强度 | 6.00 J/cm | 11.2 ft-lb/in | ASTM D256 |
| 1.20 J/cm @Temperature -30.0 °C | 2.25 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| 15.0 kJ/m2 | 7.14 ft-lb/in2 | 80*10*3; ISO 180/1A | |
| 10.0 kJ/m2 @Temperature -30.0 °C | 4.76 ft-lb/in2 @Temperature -22.0 °F | 80*10*3; ISO 180/1A | |
| 简支梁缺口冲击强度 | 1.50 J/cm2 | 7.14 ft-lb/in2 | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 1.00 J/cm2 @Temperature -30.0 °C | 4.76 ft-lb/in2 @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| 落锤总能量 | 63.0 J @Temperature 23.0 °C | 46.5 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| 线形热膨胀系数 - 流动 | 75.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 41.7 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 75.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 41.7 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| 线性热膨胀系数,横向流动 | 75.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 41.7 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |