技术参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTMD792,ISO1183 | 0.905 | g/cm³ | |
| 熔流率（熔体流动速率）(230°C/2.16kg) | ASTMD1238,ISO1133 | 11 | g/10min | ||
| 硬度 | 洛氏硬度 | ASTMD785 | 111 | ||
| 肖氏硬度(邵氏D) | ISO868 | 69 | |||
| 机械性能 | 1%正割1 | ASTMD638 | 1800 | MPa | |
| -- | ISO527-2/1A/1 | 1700 | MPa | ||
| 屈服2 | ASTMD638 | 36.0 | MPa | ||
| 屈服 | ISO527-2/1A/50 | 36.0 | MPa | ||
| 屈服3 | ASTMD638 | 9.0 | % | ||
| 屈服 | ISO527-2/1A/50 | 9.0 | % | ||
| 冲击性能 | 简支梁缺口冲击强度(23°C) | ISO179/1eA | 4.0 | kJ/m² | |
| 23°C | ASTMD256A | 25 | J/m | ||
| ISO180/1A | 3.0 | kJ/m² | |||
| 热性能 | 0.45MPa,未退火 | ASTMD648 | 95.0 | °C | |
| 0.45MPa,未退火4 | ISO75-2/Bf | 90.0 | °C | ||
| 1.8MPa,未退火 | ASTMD648 | 60.0 | °C | ||
| 1.8MPa,未退火5 | ISO75-2/Af | 55.0 | °C | ||
| -- | ASTMD1525,ISO306/A12066 | 154 | °C | ||
| ASTMD1525,ISO306/B12077 | 95.0 | °C | |||