Polycarbonate
LG Chem Ltd.
产品说明：
LUPOY PC 1201-15 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.
物性信息：
| 黄卡编号 | E67171-100907358 |
| 特性 | 低粘度 抗撞击性，良好 耐热性，高 清晰度，高 食品接触的合规性 脱模性能良好 |
| 用途 | 包装 护罩 瓶子 玩具 一次性餐具 |
| 机构评级 | FDA 21 CFR 177.1580 欧洲 食品接触, 未评级 |
| RoHS 合规性 | RoHS 合规 |
| UL文件号 | E306922 |
| 加工方法 | 挤出 注射成型 |
| 比重 | 1.20 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） (300°C/1.2 kg) | 15 | g/10 min | ASTM D1238 |
| 收缩率 - 流动 | 0.50 到 0.70 | % | ASTM D955 |
| 吸水率 | ASTM D570 | ||
| 23°C, 24 hr | 0.15 | % | ASTM D570 |
| 平衡, 23°C, 50% RH | 0.32 | % | ASTM D570 |
| 洛氏硬度 | ASTM D785 | ||
| M 级 | 73 | ASTM D785 | |
| R 级 | 118 | ASTM D785 |
| 拉伸模量 | 2340 | MPa | ASTM D638 |
| 抗张强度 | ASTM D638 | ||
| 屈服, 23°C 1 | 60.0 | MPa | ASTM D638 |
| 断裂 | 71.0 | MPa | ASTM D638 |
| 伸长率 | ASTM D638 | ||
| 屈服 | 6.0 | % | ASTM D638 |
| 断裂 | 150 | % | ASTM D638 |
| 弯曲模量 | 2410 | MPa | ASTM D790 |
| 弯曲强度 | 96.0 | MPa | ASTM D790 |
| 耐磨耗性 - Change in Haze 2 | 45 | % | ASTM D1004 |
| 平均燃烧程度 | 3 | cm | ASTM D635 |
| 悬壁梁缺口冲击强度 3(23°C, 3.20 mm) | 850 | J/m | ASTM D256 |
| 无缺口悬臂梁冲击 (23°C) | 无断裂 | ASTM D256 | |
| 装有测量仪表的落镖冲击 4(23°C, 3.20 mm, Total Energy) | 87.0 | J | ASTM D3763 |
| 载荷下热变形温度 | ASTM D648 | ||
| 0.45 MPa, 退火, 4.00 mm | 143 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 4.00 mm | 127 | °C | ASTM D648 |
| 1.8 MPa, 退火, 4.00 mm | 140 | °C | ASTM D648 |
| 维卡软化温度 | 148 | °C | ASTM D1525 5 |
| 球压温度 | > 125 | °C | IEC 60598-1 |
| 线形热膨胀系数 - 流动 (-40 到 82°C) | 6.8E-5 | cm/cm/°C | ASTM D696 |
| 体积电阻率 (23°C) | 2.0E+17 | ohms·cm | ASTM D257 |
| 介电强度 | 17 | kV/mm | ASTM D149 |
| 介电常数 (60 Hz) | 3.00 | ASTM D150 | |
| 耗散因数 (60 Hz) | 1.0E-3 | ASTM D150 | |
| 漏电起痕指数 (2.00 mm) | 250 | V | IEC 60112 |
| UL 阻燃等级 | UL 94 | ||
| 3.00 mm | HB | UL 94 | |
| 0.500 mm | V-2 | UL 94 | |
| 1.60 mm | V-2 | UL 94 | |
| 2.50 mm | V-2 | UL 94 | |
| 2.70 mm | V-2 | UL 94 | |
| 热灯丝点火温度 6(2.00 mm) | 850 | °C | IEC 60695-2-13 |
| 极限氧指数 | 26 | % | ASTM D2863 |
| 折射率 | 1.586 | ASTM D542 | |
| 透射率 | 89.0 | % | ASTM D1003 |
| 雾度 | 0.70 到 1.5 | % | ASTM D1003 |
| 1 . | 50 mm/min |
| 2 . | 1000g, 500 cycles, CS-10F Wheel |
| 3 . | 0.25 mm 缺口深度 |
| 4 . | 3.38 m/sec |
| 5 . | 速率 A (50°C/h), 载荷2 (50N) |
| 6 . | 5 sec |