PTFE 日本大金 M-18 注塑级
物性表| 表观密度 | ASTMD4894 | 0.48 | g/cm³ | |
| 收缩率 | MD | 内部方法 | 3.2 | % |
| 负载变形 | 200°C,6.9MPa | ASTMD621 | 27.0 | % |
| 25°C,14MPa | ASTMD621 | 17.2 | % | |
| 100°C,14MPa | ASTMD621 | 33.3 | % | |
| 抗张强度 | 屈服,1.50mm | ASTMD4894 | 43.0 | Mpa |
| 伸长率 | 断裂,1.50mm | ASTMD4894 | 400 | % |
| 压缩强度 | 0%应变2 | ASTMD695 | 7.80 | Mpa |
| 1%应变3 | ASTMD695 | 5.00 | Mpa | |
| 25%应变3 | ASTMD695 | 28.1 | Mpa | |
| 连续使用温度 | 260 | °C | ||
| 熔融温度 | DSC | 327 | °C | |
| 表面电阻率 | ASTMD257 | >1.0E+15 | ohms | |
| 耗散因数 | 1kHz | ASTMD150 | <1.0E-4 | |
| 介电常数 | 1kHz | ASTMD150 | <2.10 | |
| 介电强度 | 100 | KV/mm | ||
| 体积电阻率 | ASTMD257 | >1.0E+18 | ohms·cm | |
| 压缩**变形 | 25°C4 | ASTMD621 | 8.6 | % |
| 100°C4 | ASTMD621 | 20 | % | |
| 200°C5 | ASTMD621 | 16 | % | |
| MITFlexuralLife | ASTMD2178 | 5E+06 | ||
| StretchingVoidIndex | ASTMD4895 | 300 |