PPS 日本东丽 A504 增强级聚苯硫醚
A504
聚苯硫醚#|PPS
日本东丽
填充物:增强
物性信息：
| 吸水率 | 0.02 | % | ASTM D-570 |
| 比重 | 1.70 | ASTM D-792 | |
| 成形收缩率 | 东丽法 | ||
| 0.20 | % | ||
| 0.70 | % | ||
| 流动长 (320℃,98MPa,1mm厚) | 124 | ×10-3m | 东丽法 |
| 冲击强度 | ASTM D-256 | ||
| 100 | J/m | ||
| 30 | kj/m | ||
| 弯曲强度 | 205 | MPa | ASTM D-790 |
| 摩耗 | 50 | mg/1000回 | ASTM D-1044 |
| 限界PV值 | 东丽法 | kj/m.hr | 东丽法 |
| 弯曲弹性体 | 13.7 | GPa | ASTM D-790 |
| 引张强度 | 155 | MPa | ASTM D-638 |
| 冲击强度 | ASTM D-256 | ||
| 100 | J/m | ||
| 30 | kj/m | ||
| 弯曲强度 | 205 | MPa | ASTM D-790 |
| 摩耗 | 50 | mg/1000回 | ASTM D-1044 |
| 限界PV值 | 东丽法 | kj/m.hr | 东丽法 |
| 弯曲弹性体 | 13.7 | GPa | ASTM D-790 |
| 引张强度 | 155 | MPa | ASTM D-638 |
| 拉伸强度 | 1.6 | % | ASTM D-638 |
| 断裂强度 | 75 | ASTM D-732 | |
| 硬度 | 120 | 洛氏 | ASTM D-785 |
| 摩擦系数 (对钢) | 0.25 | ASTM D-1894 |
| 诱电率 (10Hz) | 3.8 | ASTM D-150 | |
| 耐电弧性W电级 | 127 | 秒 | ASTM D-495 |
| 绝缘破坏电压 | 21 | MV/m | ASTM D-149 |
| 体积固有抵抗 | 10 | Ω.m | ASTM D-257 |
| 诱电正接 (10Hz) | 0.002 | ASTM D-150 |
| 线膨张系数 | ASTM D-696 | ||
| 2.2 | ×10-5/K | ||
| 3.3 | ×10-5/K | ||
| 热变形温度 (1.82MPa) | >260 | ℃ | ASTM D-648 |
| 燃烧性 | V-0 | UL-94 | |
| 融点 | 278 | ℃ | DSC |