易流动 PC 基础创新塑料 EXL9414T-NA9G003T 抗冲击 阻燃
LEXAN™ EXL9414T resin
Polycarbonate
SABIC Innovative Plastics Asia Pacific
产品说明：
LEXAN EXL9414T resin grade is a halogen-free flame retardant polycarbonate featuring transparency, -40 degree C ductility and UL-94 V0 rating for injection molding applications. Excellent impact combined with good flow, all transparent colorability for aesthetics and thin wall flame retradancy makes this product an excellent candidate for thin wall applications.
物性信息：
| 特性 | 抗撞击性，高 良好的流动性 无卤 延展性 阻燃性 |
| 用途 | 薄壁部件 |
| 外观 | 可用颜色 清晰/透明 |
| 加工方法 | 注射成型 |
| 比重 | 1.19 | g/cm³ | ASTM D792, ISO 1183 |
| 熔流率（熔体流动速率） (300°C/1.2 kg) | 13 | g/10 min | ASTM D1238 |
| 溶化体积流率（MVR） (300°C/1.2 kg) | 12.0 | cm³/10min | ISO 1133 |
| 收缩率 - 流动 (3.20 mm) | 0.40 到 0.80 | % | 内部方法 |
| 吸水率 | ISO 62 | ||
| 饱和, 23°C | 0.12 | % | ISO 62 |
| 平衡, 23°C, 50% RH | 0.090 | % | ISO 62 |
| 拉伸模量 | |||
| -- 1 | 2180 | MPa | ASTM D638 |
| -- | 2300 | MPa | ISO 527-2/1 |
| 抗张强度 | |||
| 屈服 2 | 57.6 | MPa | ASTM D638 |
| 屈服 | 56.8 | MPa | ISO 527-2/50 |
| 断裂 3 | 59.1 | MPa | ASTM D638 |
| 断裂 | 55.3 | MPa | ISO 527-2/50 |
| 伸长率 | |||
| 屈服 4 | 5.6 | % | ASTM D638 |
| 屈服 | 5.4 | % | ISO 527-2/50 |
| 断裂 5 | 120 | % | ASTM D638 |
| 断裂 | 110 | % | ISO 527-2/50 |
| 弯曲模量 | |||
| 50.0 mm 跨距 6 | 2180 | MPa | ASTM D790 |
| -- 7 | 2120 | MPa | ISO 178 |
| 弯曲应力 | |||
| -- | 88.0 | MPa | ISO 178 |
| 屈服, 50.0 mm 跨距 8 | 92.0 | MPa | ASTM D790 |
| 简支梁缺口冲击强度 9 | ISO 179/1eA | ||
| -30°C | 60 | kJ/m² | ISO 179/1eA |
| 23°C | 70 | kJ/m² | ISO 179/1eA |
| 简支梁无缺口冲击强度 10 | ISO 179/1eU | ||
| -30°C | 无断裂 | ISO 179/1eU | |
| 23°C | 无断裂 | ISO 179/1eU | |
| 悬壁梁缺口冲击强度 | |||
| -30°C | 710 | J/m | ASTM D256 |
| 23°C | 820 | J/m | ASTM D256 |
| -30°C 11 | 55 | kJ/m² | ISO 180/1A |
| 23°C 12 | 65 | kJ/m² | ISO 180/1A |
| 无缺口伊佐德冲击强度 13 | ISO 180/1U | ||
| -30°C | 无断裂 | ISO 180/1U | |
| 23°C | 无断裂 | ISO 180/1U | |
| 装有测量仪表的落镖冲击 (23°C, Total Energy) | 75.0 | J | ASTM D3763 |
| 载荷下热变形温度 | |||
| 1.8 MPa, 未退火, 3.20 mm | 121 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 64.0 mm 跨距 14 | 116 | °C | ISO 75-2/Af |
| 维卡软化温度 | |||
| -- | 139 | °C | ASTM D1525, ISO 306/B120 11 15 |
| -- | 138 | °C | ISO 306/B50 |
| 线形热膨胀系数 | |||
| 流动 : -40 到 95°C | 6.7E-5 | cm/cm/°C | ASTM E831 |
| 流动 : 23 到 80°C | 6.7E-5 | cm/cm/°C | ISO 11359-2 |
| 横向 : -40 到 95°C | 8.0E-5 | cm/cm/°C | ASTM E831 |
| 横向 : 23 到 80°C | 8.0E-5 | cm/cm/°C | ISO 11359-2 |