法国阿科玛 PA11 BESN P40 NOIR TL 增塑剂 挤出级 管材 汽车领域
Rilsan® BESN Noir P40 TL
Polyamide 11
Arkema
产品说明：
Rilsan ® BESN Noir P40 TL is a polyamide 11 produced from a renewable source. This black grade is plasticized and designed for extrusion.
MAIN APPLICATIONS
Air brake.
Fluid transportation.
Tubing for use in motor vehicle.
物性信息：
| 添加剂 | 增塑剂 |
| 特性 | 可更新资源 |
| 用途 | 管件 汽车领域的应用 |
| 外观 | 黑色 |
| 加工方法 | 挤出 |
| 多点数据 | Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Specific Volume vs Temperature (ISO 11403-2) |
| 密度 | 1.04 | g/cm³ | ISO 1183 |
| 肖氏硬度 | ISO 868 | ||
| 邵氏 D | 68 | ISO 868 | |
| 邵氏 D, 15 秒 | 60 | ISO 868 |
| 拉伸模量 | 350 | MPa | ISO 527-2 |
| 拉伸应力 | ISO 527-2 | ||
| 屈服 | 27.0 | MPa | ISO 527-2 |
| 断裂 | 55.0 | MPa | ISO 527-2 |
| 拉伸应变 | ISO 527-2 | ||
| 屈服 | 41 | % | ISO 527-2 |
| 断裂 | > 200 | % | ISO 527-2 |
| 弯曲模量 | 350 | MPa | ISO 178 |
| 泰伯耐磨性 (1000 Cycles, 1000 g, CS-17 转轮) | 7.00 | mg | ISO 9352 |
| 简支梁缺口冲击强度 | ISO 179 | ||
| -30°C | 7.0 | kJ/m² | ISO 179 |
| 23°C | 无断裂 | ISO 179 | |
| 简支梁无缺口冲击强度 | ISO 179 | ||
| -30°C | 无断裂 | ISO 179 | |
| 23°C | 无断裂 | ISO 179 |
| 熔融温度 | 181 | °C | ISO 11357-3 |
| ISO Shortname | PA11-P, EHL, 22-003 | ISO 1874 | |
| Renewable Carbon Conent | > 88 | % | ASTM D6866 |
| 干燥温度 | 80.0 到 90.0 | °C | |
| 干燥时间 | 4.0 到 8.0 | hr | |
| 熔体温度 | 230 到 280 | °C |