| 密度 | 1.01 g/cm³ | ISO 1183 | Dry |
| 收缩率 | |||
| 纵向(Flow) | 1.2 % | ISO 294-4, 2577 | Dry |
| 横向(Across Flow) | 1.4 % | ISO 294-4, 2577 | Dry |
| 吸水率 | 1.1 % | ISO 62 | Dry |
| 吸湿率 | 0.7 % | ISO 62 | Dry |
| 拉伸强度 | |||
| 屈服(yld) | 18 Mpa | ISO 527-1/-2 | Cond. |
| 屈服(yld) | 19 Mpa | ISO 527-1/-2 | Dry |
| 拉伸延伸率 | |||
| 屈服(yld) | 22 % | ISO 527-1/-2 | Cond. |
| 屈服(yld) | 22 % | ISO 527-1/-2 | Dry |
| 标称断裂伸长率 | 50 % | ISO 527-1/-2 | Cond. |
| 标称断裂伸长率 | 50 % | ISO 527-1/-2 | Dry |
| 拉伸模量 | 285 Mpa | ISO 527-1/-2 | Cond. |
| 拉伸模量 | 307 Mpa | ISO 527-1/-2 | Dry |
| 简支梁缺口(Charpy Notched) | |||
| -30℃ (-22℉) | 20 kJ/m² | ISO 179/1eA | Cond. |
| 23℃ (73℉) | NB kJ/m² | ISO 179/1eA | Cond. |
| 简支梁无缺口(Charpy Unnotched) | |||
| -30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | Cond. |
| 23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Cond. |
| 邵氏硬度 D | 58 D | ISO 7619-1 | Dry, 15s |
| 维卡软化温度(Vicat) | 157 °C | ISO 306 | Dry, 50°C/h 50N |
| 熔融温度(Tm) | 169 °C | ISO 11357-1/-3 | Dry, 10°C/min |
| 加工温度 | 260 °C | - | Injection molding |
| 模具温度 | 60 °C | - | Injection |