TAIRIREX GP5250 物性表
机构评级 | EC 1907/2006 (REACH) |
RoHS 合规性 | RoHS 合规 |
UL文件号 | E162823 |
形式 | 粒子 |
加工方法 | 注射成型 |
比重 | |||
-- | 1.04 | g/cm? | ASTM D792 |
23°C | 1.04 | g/cm? | ISO 1183 |
熔流率(熔体流动速率) (200°C/5.0 kg) | 7.0 | g/10 min | ASTM D1238, ISO 1133 |
抗张强度 | |||
23°C | 42.2 | MPa | ASTM D638 |
23°C | 42.0 | MPa | ISO 527-2 |
伸长率 (断裂, 23°C) | 2.0 | % | ASTM D638, ISO 527-2 |
弯曲模量 (23°C) | 3330 | MPa | ASTM D790, ISO 178 |
弯曲强度 (23°C) | 78.0 | MPa | ASTM D790, ISO 178 |
无缺口悬臂梁冲击 (23°C, 6.35 mm) | 17 | J/m | ISO 180, ASTM D256 |
载荷下热变形温度 1(1.8 MPa, 退火, 3.18 mm) | 87.0 | °C | ASTM D648, ISO 75-2/A |
维卡软化温度 | 94.0 | °C | ASTM D1525, ISO 306/B |