高冲击 韩国LG PC 1201-10 中粘度 易脱模 食品包装 玩具应用
1201-10
聚碳酸酯#防弹胶|PC
LG化学
产品用途:玩具、食品器皿、包装应用
填充物:食品包装 注塑
物性信息：
| 密度 | 1200 | kg/m | ASTM D-792 |
| 吸水率 (24hr,23℃) | 0.15 | % | ASTM D-570 |
| 平衡吸水率 (23℃,相对湿度50%) | 0.32 | % | ASTM D-570 |
| 熔体流动速率 | 10 | g/10min | ASTM D-1238 |
| 比重 | 1.20 | ASTM D-792 | |
| 折射率 | 1.586 | ASTM D-542 | |
| 模具收缩率 | 0.005-0.007 | mm/mm | ASTM D-955 |
| 透光率 | 89 | % | ASTM D-1003 |
| 雾度 | 0.7-1.5 | % | ASTM D-1003 |
| 缺口冲击强度 (23℃) | 900 | J/m | ASTM D-256 |
| 冲击强度 (23℃) | 未破裂 | ASTM D-256 | |
| 洛氏硬度 | 73 | M标度 | ASTM D-785 |
| 拉伸强度 | ASTM D-638 | ||
| 60 | MPa | ||
| 71 | MPa | ||
| 弯曲强度 | 96 | MPa | ASTM D-790 |
| 拉伸模量 | 2410 | MPa | ASTM D-638 |
| 弯曲模量 | 2410 | MPa | ASTM D-790 |
| 伸长率 | ASTM D-638 | ||
| 60 | % | ||
| 150 | % | ||
| 落锤冲击强度 (23℃) | 87 | J | ASTM D-3763 |
| 介电强度 (60HZ) | 17 | kv/mm | ASTM D-149 |
| 对比电弧径迹指数 (2mm) | 250 | v | IEC 112 |
| 辉光灯丝测试 (2mm) | 850 | ℃ | IEC 695-2-1 |
| 损耗因素 (60Hz) | 0.001 | ASTM D-150 | |
| 体积电阻率 (23℃,干) | 2.0×10 | Ω.cm | ASTM D-257 |
| 热变形温度 | ASTM D-648 | ||
| (退火@0.45MPa(4 mm)) | 144 | ℃ | |
| (退火@1.82MPa(4 mm)) | 141 | ℃ | |
| 球状压良温度 | >125 | ℃ | IEC 598-1 |
| 线性热收缩率 (-40℃-82℃) | 68×10-6 | mm/mm/℃ | ASTM D-696 |
| 平均燃烧程度 | 25 | mm | ASTM D-635 |
| 热变形温度 (未退火@1.82MPa(4 mm)) | 128 | ℃ | ASTM D-648 |
| 维卡软化点 (50 C/hour) | 149 | ℃ | ASTM D-1525 |
| 需氧系数 | 26 | % | ASTM D-2863 |
| 阻燃性 | UL 94 | ||
| (1.5mm) | V-2 | ||
| (1.6mm) | V-2 | ||
| (2.5-2.7mm) | V-2 | ||
| (3.0mm) | HB |