聚甲醛(POM)共聚物
FORMOCON® FM090 物性表
| 比重 | 1.41 | g/cm3 | ASTM D792 |
| 熔流率(熔体流动速率) (190°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| 收缩率 - 流动 (3.00 mm) | 1.8 到 2.2 | % | ASTM D955 |
| 吸水率 (平衡, 23°C, 69%RH) | 0.22 | % | ASTM D570 |
| 抗张强度 (屈服) | 60.8 | MPa | ASTM D638 |
| 伸长率 (断裂) | 60 | % | ASTM D638 |
| 弯曲模量 | 2550 | MPa | ASTM D790 |
| 弯曲强度 | 93.2 | MPa | ASTM D790 |
| 压缩强度 | ASTM D695 | ||
| 1% 应变 | 31.4 | MPa | ASTM D695 |
| 10% 应变 | 108 | MPa | ASTM D695 |
| 载荷下热变形温度 | ASTM D648 | ||
| 0.45 MPa, 未退火 | 158 | °C | ASTM D648 |
| 1.8 MPa, 未退火 | 110 | °C | ASTM D648 |
| 维卡软化温度 | 162 | °C | ASTM D1525 |
| 熔融温度 | 165 | °C | DSC |
| 线形热膨胀系数 - 流动 | 8.5E-5 | cm/cm/°C | ASTM D696 |
| UL 阻燃等级 | HB | UL 94 |