LEXAN™ LUX2614G resin
Polycarbonate
SABIC Innovative Plastics Europe
产品说明：
LEXAN LUX2614G (EXRL0944) is a diffusive, high viscosity, uv stabilized, flame retardant polycarbonate with improved light transmission and providing good colorstability under heat exposure. Developed for injection molding LED applications
物性信息：
| 黄卡编号 | E45329-101040015 |
| 添加剂 | 紫外线稳定剂 |
| 特性 | 良好的颜色稳定性 粘度，高 阻燃性 |
| 用途 | LEDs |
| RoHS 合规性 | RoHS 合规 |
| 加工方法 | 注射成型 |
| 比重 | ASTM D792 | ||
| -- | 1.20 | g/cm³ | ASTM D792 |
| -- | 1.19 | g/cm³ | ASTM D792 |
| 特定体积 | 0.830 | cm³/g | ASTM D792 |
| 熔流率（熔体流动速率） (300°C/1.2 kg) | 7.0 | g/10 min | ASTM D1238 |
| 溶化体积流率（MVR） (300°C/1.2 kg) | 7.00 | cm³/10min | ISO 1133 |
| 收缩率 - 流动 (3.20 mm) | 0.50 到 0.70 | % | 内部方法 |
| 吸水率 | ASTM D570 | ||
| 24 hr | 0.15 | % | ASTM D570 |
| 平衡, 23°C | 0.35 | % | ASTM D570 |
| 平衡, 100°C | 0.58 | % | ASTM D570 |
| 室外适用性 | f2 | UL 746C |
| 洛氏硬度 | ASTM D785 | ||
| M 级 | 70 | ASTM D785 | |
| R 级 | 118 | ASTM D785 |
| 拉伸模量 | 2300 | MPa | ISO 527-2/1 |
| 抗张强度 | |||
| 屈服 1 | 62.1 | MPa | ASTM D638 |
| 屈服 | 63.0 | MPa | ISO 527-2/50 |
| 断裂 2 | 65.5 | MPa | ASTM D638 |
| 断裂 | 63.0 | MPa | ISO 527-2/50 |
| 伸长率 | |||
| 屈服 3 | 7.0 | % | ASTM D638 |
| 屈服 | 6.0 | % | ISO 527-2/50 |
| 断裂 4 | 110 | % | ASTM D638 |
| 弯曲模量 | |||
| 50.0 mm 跨距 5 | 2340 | MPa | ASTM D790 |
| -- 6 | 2300 | MPa | ISO 178 |
| 弯曲应力 | |||
| -- | 94.0 | MPa | ISO 178 |
| 屈服, 50.0 mm 跨距 7 | 93.1 | MPa | ASTM D790 |
| 泰伯耐磨性 (1000 Cycles, 1000 g, CS-17 转轮) | 10.0 | mg | ASTM D1044 |