Makrolon® AL2647
Polycarbonate
Covestro - Polycarbonates
产品说明：
MVR (300 °C/1.2 kg) 12 cm³/10 min; Automotive lighting; medium viscosity; UV stabilized; easy release; injection molding - melt temperature 280 - 320 °C; available in clear transparent colors and in various signal colors; headlamp lenses for automotive forward lighting
物性信息：
| 黄卡编号 | E41613-233169 |
| 添加剂 | 紫外线稳定剂 |
| 特性 | 脱模性能良好 中等粘性 |
| 用途 | Lighting Applications 汽车领域的应用 |
| RoHS 合规性 | RoHS 合规 |
| 外观 | 可用颜色 清晰/透明 |
| 加工方法 | 注射成型 |
| 多点数据 | Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Specific Volume vs Temperature (ISO 11403-2) Viscosity vs. Shear Rate (ISO 11403-2) |
| 密度 (23°C) | 1.20 | g/cm³ | ISO 1183 |
| 表观密度 1 | 0.66 | g/cm³ | ISO 60 |
| 熔流率（熔体流动速率） (300°C/1.2 kg) | 13 | g/10 min | ISO 1133 |
| 溶化体积流率（MVR） (300°C/1.2 kg) | 12.0 | cm³/10min | ISO 1133 |
| 收缩率 | |||
| 垂直流动方向 | 0.60 到 0.80 | % | ISO 2577 |
| 流动方向 | 0.60 到 0.80 | % | ISO 2577 |
| 垂直流动方向 : 2.00 mm 2 | 0.75 | % | ISO 294-4 |
| 流动方向 : 2.00 mm 3 | 0.70 | % | ISO 294-4 |
| 吸水率 | ISO 62 | ||
| 饱和, 23°C | 0.30 | % | ISO 62 |
| 平衡, 23°C, 50% RH | 0.12 | % | ISO 62 |
| 球压硬度 | 115 | MPa | ISO 2039-1 |
| 拉伸模量 (23°C) | 2400 | MPa | ISO 527-2/1 |
| 拉伸应力 | ISO 527-2/50 | ||
| 屈服, 23°C | 67.0 | MPa | ISO 527-2/50 |
| 断裂, 23°C | 70.0 | MPa | ISO 527-2/50 |
| 拉伸应变 | ISO 527-2/50 | ||
| 屈服, 23°C | 6.1 | % | ISO 527-2/50 |
| 断裂, 23°C | 130 | % |