现货供应 日本东丽 PBT 1401X06 热稳定 用于紧固件 连接器 外壳应用
1401X06
聚对苯二甲酸丁二醇酯#聚酯|PBT
日本东丽
物性信息：
| 吸水率 (23℃·24小时) | 0.08 | % | ASTM D-570 |
| 泰伯磨耗量 (1.000g·CS-17) | 10 | 毫克/1.000m | ASTM D-1044 |
| 比重 | 1.31 | ASTM D-792 | |
| 膜塑收缩 (80×80×3板材) | 1.7-2.3 | % | |
| 磨擦系数 | ASTM D-1894 | ||
| 0.13 | |||
| 0.17 | |||
| 负荷下的 | ASTM D-648 | ||
| 154 | ℃ | ||
| 58 | ℃ |
| 弯曲强度 (23℃) | 900 | kg/cm | ASTM D-790 |
| 拉伸强度 (23℃) | 600 | kg/cm | ASTM D-638 |
| 弯曲模量 (23℃) | 26 | kg/cm×10 | ASTM D-790 |
| 洛氏硬度 | 75 | M标度 | ASTM D-785 |
| 断裂拉伸伸长 (23℃) | 15 | % | ASTM D-638 |
| IZOD冲击强度 | ASTM D-256 | ||
| (23℃) | 不破裂 | kg·cm/cm | |
| (-40℃) | 120 | kg·cm/cm | |
| (23℃) | 4.4 | kg·cm/cm | |
| (-40℃) | 3.5 | kg·cm/cm | |
| 压缩强度 (23℃) | 900 | kg/cm | ASTM D-695 |
| 体积电阻率 | 4.0 | cm×10 | ASTM D-257 |
| 介电强度 (短时·23℃·1/8时) | 17 | kV/mm | ASTM D-149 |
| 抗电弧性 | 144 | 秒 | ASTM D-495 |
| 线性热膨胀 | 9.4 | cm/cm℃×10 | ASTM D-696 |