观看PC 美国RTP 383 FRA 增强20%碳纤 耐冲击 汽车外壳 零件应用视频:
技术参数密度 | 1.3 g/cm³ | ASTM D792 | |
收缩率 | |||
- | 0.03~0.15 % | ASTM D 955 | 3.2 mm |
吸水率 | 0.1 % | ASTM D570 | 24 hrs, 23°C |
填充/灰分 | 20 % | Internal | |
拉伸强度 | |||
- | 138 Mpa | ASTM D 638 | |
拉伸延伸率 | |||
- | 1.5~2.5 % | ASTM D 638 | |
弯曲强度 | |||
- | 207 Mpa | ASTM D790 | |
弯曲模量 | 12066 Mpa | ASTM D790 | |
拉伸模量 | 12756 Mpa | ASTM D638 | |
悬臂梁缺口(Izod Notched) | |||
- | 96 J/m | ASTM D 256 | 3.2 mm |
悬臂梁无缺口(Izod Unnotched) | |||
- | 534 J/m | ASTM D 4812 | 3.2 mm |
洛氏硬度R | 118 R | ASTM D785 | |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)(4.6kg/cm²) | 149 °C | ASTM D648 | |
1.8 Mpa (264 psi)(18.6kg/cm²) | 146 °C | ASTM D648 | |
UL 防火等级 | |||
V-0 | 1.5 mm | ASTM D3801 | |
体积电阻率 |