阻燃PC/ABS 美国RTP EMI 2563 FR 增强20%不锈钢 挡板应用

比重

1.51

g/cm³

收缩率 - 流动 (3.20 mm)

0.30 到 0.60

%

含水量

0.020

%

拉伸模量

4140

MPa

抗张强度

66.9

MPa

伸长率 (屈服)

1.0 到 3.0

%

弯曲模量

4140

MPa

弯曲强度

123

MPa

悬壁梁缺口冲击强度 (3.20 mm)

37

J/m

无缺口悬臂梁冲击 (3.20 mm)

370

J/m

载荷下热变形温度 (1.8 MPa, 未退火)

110

°C

表面电阻率

体积电阻率

< 1.0

ohm·cm

Static Decay

< 0.5

sec

UL 阻燃等级

Primary Additive

20

%

干燥温度

93.3

°C

干燥时间

4.0

hr

Dew Point

-28.9

°C

加工（熔体）温度

243 到 274

°C

模具温度

51.7 到 93.3

°C

注塑压力

68.9 到 103

MPa

Use a reverse barrel profile. Remove hopper magnets. Allow 4 - 5 shots to properly disperse the conductive fibers. The surface finish should have a silver streaking appearance, not clumps.
Use a reverse barrel profile. To maximize fiber length, the following injection barrel, screw, and tip designs should be followed. L/D ratio 16/1 - 22/1, Compression ratio 2:1, Flight depth 0.200 in (5 mm) minimum, in feed section, Screw diameter 0.65 - 0