基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 增韧/冲击改性填充增强 | |||
| 添加助剂 | 抗冲击剂 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 10% 碳酸钙 | |||
| 密度 | 0.97 g/cm³ | ASTM D792 | |
| 收缩率 | |||
| - | 1.5~1.9 % | ASTM D 955 | 3.2 mm |
| 填充/灰分 | 10 % | Internal | |
| 拉伸强度 | |||
| - | 25 Mpa | ASTM D 638 | |
| 拉伸延伸率 | |||
| - | 10 % | ASTM D 638 | |
| 弯曲强度 | |||
| - | 33 Mpa | ASTM D790 | |
| 弯曲模量 | 1241 Mpa | ASTM D790 | |
| 拉伸模量 | 1517 Mpa | ASTM D638 | |
| 悬臂梁缺口(Izod Notched) | |||
| - | 160 J/m | ASTM D 256 | 3.2 mm |
| 悬臂梁无缺口(Izod Unnotched) | |||
| - | 1602 J/m | ASTM D 4812 | 3.2 mm |
| 热变形温度(HDT) | |||
| 1.8 Mpa (264 psi)（18.6kg/cm²） | 49 °C | ASTM D648 | |
| UL 防火等级 | |||
| HB | 1.5 mm | ASTM D 635 |