| MeltViscosity | 200°C,1000sec^-1 | ASTMD3835 | 320 | Pa·s |
| 密度 / 比重 | ASTMD792 | 1.19 | g/cm³ | |
| 密度 / 比重 | ISO1183 | 1.19 | g/cm³ | |
| 熔体质量流动速率 | 230°C/3.8kg | ASTMD1238 | 3.3 | g/10min |
| 熔体质量流动速率 | 220°C/5.0kg | ISO1133 | 7.0 | g/10min |
| 熔体体积流动速率 | 220°C/10.0kg | ISO1133 | 40.0 | cm3/10min |
| 收缩率 | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| 拉伸模量2 | ASTMD638 | 2070 | Mpa | |
| 拉伸模量 | ISO527-2/1 | 2210 | Mpa | |
| 抗张强度3 | 屈服 | ASTMD638 | 37.9 | Mpa |
| 拉伸应力 | 屈服 | ISO527-2/50 | 41.1 | Mpa |
| 抗张强度3 | 断裂 | ASTMD638 | 30.3 | Mpa |
| 伸长率3 | 屈服 | ASTMD638 | 2.4 | % |
| 伸长率4 | 断裂 | ASTMD638 | 17 | % |
| 拉伸应变 | 断裂 | ISO527-2/50 | 22 | % |
| 弯曲模量4 | 50.0mm跨距 | ASTMD790 | 2340 | Mpa |
| 弯曲模量5 | ISO178 | 2260 | Mpa | |
| 弯曲强度5,6 | ISO178 | 63.3 | Mpa | |
| 弯曲强度4 | 屈服,50.0mm跨距 | ASTMD790 | 67.6 | Mpa |