| 熔流率（熔体流动速率） | 230°C/3.8 kg | ASTM D1238 | 3.3 | g/10 min |
| 熔流率（熔体流动速率） | 220°C/5.0 kg | ISO 1133 | 7.0 | g/10 min |
| 熔融体积流量（MVR） | 220°C/10.0 kg | ISO 1133 | 40.0 | cm3/10min |
| 收缩率 - 流动 | 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| 拉伸模量 | -- 2 | ASTM D638 | 2060 | Mpa |
| 拉伸模量 | -- | ISO 527-2/1 | 2210 | Mpa |
| 抗张强度 | 屈服 3 | ASTM D638 | 37.0 | Mpa |
| 抗张强度 | 屈服 | ISO 527-2/50 | 41.0 | Mpa |
| 抗张强度 | 断裂 3 | ASTM D638 | 30.0 | Mpa |
| 伸长率 | 屈服 3 | ASTM D638 | 2.4 | % |
| 伸长率 | 断裂 3 | ASTM D638 | 17 | % |
| 伸长率 | 断裂 | ISO 527-2/50 | 22 | % |
| 弯曲模量 | 50.0 mm 跨距 4 | ASTM D790 | 2340 | Mpa |
| 弯曲模量 | -- 5 | ISO 178 | 2260 | Mpa |
| 弯曲应力 | -- 5, 6 | ISO 178 | 63.0 | Mpa |
| 弯曲应力 | 屈服, 50.0 mm 跨距 4 | ASTM D790 | 67.0 | Mpa |
| 载荷下热变形温度 | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 86.0 | °C |
| 载荷下热变形温度 | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 75.0 | °C |
| 维卡软化温度 | -- | ASTM D15258 | 93.0 | °C |
| 维卡软化温度 | -- | ISO 306/B50 | 92.0 | °C |
| 线形热膨胀系数 | 流动 : -40 到 40°C | ASTM E831 | 9.0E-5 | cm/cm/°C |
| 线形热膨胀系数 | 横向 : -40 到 40°C | ASTM E831 | 9.2E-5 | cm/cm/°C |
| RTI Elec | UL 746 | 90.0 | °C |