CYCOLOY™ C1200HF resin
Polycarbonate + ABS
SABIC Innovative Plastics
产品说明：
PC+ABS, excellent flow/impact/high heat resistance. Low temperature ductility. For automotive, appliance and electrical components.
物性信息：
| 黄卡编号 | E121562-221028 |
| 特性 | 抗撞击性，良好 良好的流动性 耐热性，高 延展性 |
| 用途 | 电气/电子应用领域 家电部件 汽车领域的应用 |
| 加工方法 | 注射成型 |
| 多点数据 | Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Elastic Modulus vs Temperature (ASTM D4065) Flexural DMA (ASTM D4065) Instrumented Impact (Energy) (ASTM D3763) Instrumented Impact (Load) (ASTM D3763) Pressure-Volume-Temperature (PVT - Zoller Method) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Creep (ASTM D2990) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) Viscosity vs. Shear Rate (ASTM D3835) |
| 比重 | 1.15 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） (260°C/5.0 kg) | 19 | g/10 min | ASTM D1238 |
| 溶化体积流率（MVR） (265°C/5.0 kg) | 24.0 | cm³/10min | ISO 1133 |
| 收缩率 - 流动 (3.20 mm) | 0.50 到 0.70 | % | 内部方法 |
| 拉伸模量 | |||
| -- 1 | 2280 | MPa | ASTM D638 |
| -- | 2370 | MPa | ISO 527-2/1 |
| 抗张强度 | |||
| 屈服 2 | 57.2 | MPa | ASTM D638 |
| 屈服 | 55.0 | MPa | ISO 527-2/50 |
| 伸长率 | |||
| 屈服 3 | 5.0 | % | ASTM D638 |
| 屈服 | 4.8 | % | ISO 527-2/50 |
| 断裂 4 | 150 | % | ASTM D638 |
| 断裂 | 110 | % | ISO 527-2/50 |
| 弯曲模量 | |||
| 50.0 mm 跨距 5 | 2340 | MPa | ASTM D790 |
| -- | 2250 | MPa | ISO 178 |
| 弯曲应力 | |||
| -- | 86.0 | MPa | ISO 178 |
| 屈服, 50.0 mm 跨距 6 | 88.3 | MPa | ASTM D790 |
| 悬壁梁缺口冲击强度 | |||
| -30°C | 480 | J/m | ASTM D256 |
| 23°C | 590 | J/m | ASTM D256 |
| -30°C 7 | 34 | kJ/m² |