CYCOLOY™ C6200 resin
Polycarbonate + ABS
SABIC Innovative Plastics
产品说明：
Non-chlorinated, nombrominated flame retardant PC/ABS offering balanced heat, flow and impact to meet various application needs.
物性信息：
| 黄卡编号 | E121562-221037 |
| 添加剂 | 阻燃性 |
| 特性 | Chlorine Free 抗撞击性，良好 良好的流动性 耐热性，中等 无溴 阻燃性 |
| 加工方法 | 注射成型 |
| 多点数据 | Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Elastic Modulus vs Temperature (ASTM D4065) Flexural DMA (ASTM D4065) Pressure-Volume-Temperature (PVT - Zoller Method) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Creep (ASTM D2990) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) Viscosity vs. Shear Rate (ASTM D3835) |
| 比重 | 1.18 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） (260°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Spiral Flow | 68.6 | cm | 内部方法 |
| 收缩率 | 内部方法 | ||
| 流动 : 3.20 mm | 0.40 到 0.60 | % | 内部方法 |
| 横向流动 : 3.20 mm | 0.40 到 0.60 | % | 内部方法 |
| 抗张强度 1(屈服) | 66.9 | MPa | ASTM D638 |
| 伸长率 2(断裂) | 50 | % | ASTM D638 |
| 弯曲模量 3(100 mm 跨距) | 2690 | MPa | ASTM D790 |
| 弯曲强度 4(屈服, 100 mm 跨距) | 103 | MPa | ASTM D790 |
| 悬壁梁缺口冲击强度 (23°C) | 530 | J/m | ASTM D256 |
| 装有测量仪表的落镖冲击 | ASTM D3763 | ||
| -30°C, Energy at Peak Load | 54.2 | J | ASTM D3763 |
| 23°C, Energy at Peak Load | 61.0 | J | ASTM D3763 |
| 载荷下热变形温度 | ASTM D648 | ||
| 1.8 MPa, 未退火, 3.20 mm | 87.8 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 6.40 mm | 90.6 | °C | ASTM D648 |
| RTI Elec | 85.0 | °C | UL 746 |
| RTI Imp | 85.0 | °C | UL 746 |
| RTI | 85.0 | °C | UL 746 |